High Toughness Ps Extrusion Chimei Ph-88 High Impact Hips Blown...
In Stock
₵24.46
Wholesale MOQ: 2+
Specifications and models
Estimated Shipping
Air Express
3–7 days
Air Normal
12–16 days
Sea Freight
50–60 days
Secure Payment
Encrypted payment via Hubtel.
C2G Managed Shipping
We handle procurement and direct shipping to Ghana.
Product Details & Specifications
- Origin: Chimei, taiwan
- Country/region of origin: China
- Manufacturer (place of origin): Chimei, taiwan
- Item number: 00022
- Brand: PH-88
- Properties level: High impact resistance
- Usage level: Sports equipment
- Brand: Chimei, taiwan
- Specifications and models: PH-88
- Product unit price: 11.40
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 200°C/5.0 kg | 6.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 16 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (200°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (L 计秤) | 60 | ASTM D785 | |
| 球压硬度 (H 358/30) | 84.0 | MPa | ISO 2039-1 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | |||
| 屈服 | 27.0 | MPa | ISO 527-2/50 |
| 断裂 | 22.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 23.5 | MPa | ASTM D638 |
| 伸长率 | |||
| 断裂, 3.00 mm 2 | 40 | % | ASTM D638 |
| 断裂 | 56 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 6.00 mm 3 | 1960 | MPa | ASTM D790 |
| -- 4 | 1200 | MPa | ISO 178 |
| 弯曲强度 | |||
| 6.00 mm 5 | 37.3 | MPa | ASTM D790 |
| -- 6 | 35.0 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | |||
| -- | 11 | kJ/m² | ISO 179 |
| -- | 12 | kJ/m² | ISO 179/2C |
| 简支梁无缺口冲击强度 | 100 | kJ/m² | ISO 179/2U |
| 悬壁梁缺口冲击强度 | |||
| 23°C, 3.00 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 83 | J/m | ASTM D256 |
| -- | 10 | kJ/m² | ISO 180/1A |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火 | 80.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 74.0 | °C | ISO 75-2/A |
| 1.8 MPa, 退火 | 94.0 | °C | ASTM D648 |
| 1.8 MPa, 退火 | 89.0 | °C | ISO 75-2/A |
| 维卡软化温度 | |||
| -- | 98.0 | °C | ASTM D1525, ISO 306/A120 6 7 |
| -- | 96.0 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| -- | 89.0 | °C | ISO 306/B120 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 2.0 到 3.0 | hr | |
| 料筒后部温度 | 160 到 180 | °C | |
| 料筒中部温度 | 180 到 200 | °C | |
| 料筒前部温度 | 180 到 200 | °C | |
| 模具温度 | 40.0 到 70.0 | °C |
| 备注 | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 速率 A (50°C/h) |
高抗冲击级聚苯乙烯（HIPS）可注塑或挤塑成各种制品，适合家电产品外壳，电器用品、仪器仪表配件、冰箱内衬、板材、电视机、收录机、电话机壳体、文教用品、玩具、包装容器、日用品、家具、餐具、托盘、餐具、结构泡沫制品等。
聚苯乙烯（PS）的成型加工
聚苯乙烯流动性好，加工性能好，易着色，尺寸稳定性好。可用注塑、挤塑、吹塑、发泡、热成型、粘接、涂覆、焊接、机加工、印刷等方法加工成各种制件。特别适用于注塑成型，注塑成型时物料一般可不经过干燥直接使用。但为了提高透明产品质量，可在55℃~70℃鼓风烘箱内预干燥1~2h。具体加工条件大致为：料筒温度200℃左右，模具温度60~80℃，注塑温度170℃至220℃，注塑压力比为1.6~4.0。成型后的制品应在红外线灯或鼓风烘箱内，于 70℃恒温处理2~4h。